ZG-P-5050/ZG-I-8618
Número do produto
Classificação
Material de alta densidade e baixa dureza
Quantidade
-
+
Estoque:
Product description
Parâmetro
牌号( Shop sign): ZG-P-493/ZG-I-338
低硬度，低密度，聚醚型鞋垫鞋底原液
1.特性：低硬度，低密度，聚醚型
Characteristics:Low hardness，low density，Polyether insoles.
2.用途：适用于聚醚鞋垫的生产
Application：Applicable for the production of polyether insoles for men and women.
3. 原液特性Typical properties of PU Resin
| 品名 | 外观 | 粘度（Pa·s/50℃） | 密度（g/cm3/40℃） | 包装（kg） |
| ZG-P-493 | 白色或淡黄，液状无异物White or pale yellow, liquid, no foreign material | 0.30-0.70 | 1.00-1.05 | 18 |
|
ZG-I-338
|
透明液体无异物Transparent liquid, no foreign material | 0.10-0.30 | 1.00-1.05 | 20 |
参考发货配比(Reference shipments ratio)：A/B=33/20(桶)
Reference shipments ratio: A/B=33/20(barrel)
| 测试项目Test item | 参考物性值Reference physical properties |
| 鞋底成型密度Molded density of sole（g/cm3） | 0.3-0.4 |
| 硬度(A型)Hardness (type A) | 10-25 |
| 拉伸强度Tensile strength（MPa） | 2.0-3.0 |
| 伸长率Elongation（％） | 350-550 |
| NBS耐磨NBS abrasion resistance（％） | ≥10% |
| 自由泡密度Free foam density（g/cm3） | 0.22-0.36 |
| 耐折性(常温）(4万次裂口长度，mm)Folding endurance (room temperature)(40,000 gap length mm) | ＜8 |
4. 成型条件及物性值(Molding conditions & physical properties)：
●配合比率是以最佳配比值为基础，此配比值会随添加的颜料助剂种类和添加量不同而变化。
Matching ratio is based on the optimal matching value which will vary with the category and additive amount of paint additives added.
●自由泡沫密度会依季节（温度，湿度）的不同而变化。
Free foam density will vary with the seasons (temperature, humidity).
●脱模时间会随成型品厚度的增加而延长。
Stripping time will be extended with the increase of the thickness of moldings.
●耐折条件：屈挠角度为 90度，频率为80次/min*4万次。
Folding endurance conditions: bending angle is 90 degrees and the frequency is 80 times / min * 40 thousand times
● 以上数据仅作参考，具体数据以实际操作为准。如需其他物性指标，请与我公司联系。
Data listed above is just for reference. The specific data is subjected to the practical operation. If other physical properties are required, please contact us.