Concentramo-nos em poliuretano para sola de sapatos
ZG-P-5080/ZG-I-5002
牌号( Shop sign): ZG-P-5080/ZG-I-5002
1. 特性:中硬度,中高密度
Application: Meduim to High hardness, Meduim to High density.
2. 用途:适用于男女休闲鞋,皮鞋鞋底的生产
Characteristic:. Suitable for female high-heeled shoes production
3. 原液特性Typical properties of pu resin
品 名 Name of products |
外 观 Appearance |
粘 度Viscosity(Pa·s/50℃) | 密 度Density(g/cm3/40℃) | 包 装Packge(kg) |
ZG-P-5080 | 白色或淡黄,液状无异物White or pale yellow,liquid foreign material | 0.40-0.80 | 1.16-1.20 | 18 |
ZG-I-5002 | 透明液体无异物Tranparent and pure liquid | 0.10-0.30 | 1.18-1.20 | 20 |
参考发货配比(Reference shipments ratio):A/B=27/26(桶)
4. 成型条件及物性值(Typical processing parameters& Typcal properties):
测试项目Test item | 参考物性值Physical properties |
鞋底成型密度Molded density(g/cm3) | 0.45~0.55 |
硬度(A型)Hardness(type A) | 40~55 |
拉伸强度Tensile strength(MPa) | 3.0~5.0 |
伸长率Elingation(%) | 300~400 |
NBS耐磨Wear(%) | ≥10% |
自由泡密度Free rise foam density(g/cm3) | 0.25~0.30 |
耐折性(常温)(4万次裂口长度,mm)Folding(room temperature)(40,000 gap length mm) | <8 |
●配合比率是以最佳配比值为基础,此配比值会随添加的颜料助剂种类和添加量不同而变化。
With the best ratio is based on the ratio, the ratio of value added with The type and quantity of paint additives vary.
●自由泡沫密度会依季节(温度,湿度)的不同而变化。
the free foam density according to the seasons (temperature, humidity) vary
●脱模时间会随成型品厚度的增加而延长。
Ejection time with the increase of the thickness of molded extension
●耐折条件:屈挠角度为 90度,频率为80次/min*4万次。
Folding conditions: angle of 90 degrees of flex, frequency of 80 times / min * 4 million
● 以上数据仅作参考,具体数据以实际操作为准。如需其他物性指标,请与我公司联系。
Data listed above are just for reference .The detail data are subjected to practical operation.If other requests for physical properties,please contact us.