Concentramo-nos em poliuretano para sola de sapatos
ZG-P-8130/ZG-I-8260
中硬度中高密度聚氨酯耐寒鞋鞋底原液
牌号(Shop sign): ZG-P-8130/ZG-I-8260
耐寒鞋鞋底原液
PU Resin for shoe sole of cold-resistant shoes
1. 特性：中硬度，中高密度。耐寒，半耐寒。
Characteristic: Medium hardness, medium and low density, cold resistance and semi cold resistance
2. 用途：适用于耐寒，半耐寒男女鞋底的生产。
Application: Applicable to the production of cold-resistant and half hardy soles for both men and women shoes
3. 原液特性Typical properties of PU Resin
3. 原液特性Typical properties of PU Resin
|
品 名 Name of products |
外 观 Appearance |
粘 度Viscosity（Pa·s/50℃） | 密 度Density（g/cm3/40℃） | 包 装Package（kg） |
| ZG-P-8130 | 白色或淡黄，液状无异物White or pale yellow, liquid, no foreign material | 1.00-1.40 | 1.16-1.20 | 18 |
| ZG-I-8260 | 透明液体无异物Transparent liquid, no foreign materials | 0.20-0.40 | 1.18-1.20 | 20 |
参考发货配比(Reference shipments ratio)：A/B=30/24(桶)
Reference shipments ratio: A/B=30/24(barrel)
4. 成型条件及物性值(Molding conditions & physical properties)：
| 测试项目Test item | 参考物性值Reference physical properties |
| 鞋底成型密度Molded density of sole（g/cm3） | 0.25~0.65 |
| 硬度(A型)Hardness (type A) | 35~65 |
| 拉伸强度Tensile strength（MPa） | 3.5~4.5 |
| 伸长率Elongation（％） | 250~550 |
| NBS耐磨NBS abrasion resistance （％） | ≥10% |
| 自由泡密度Free foam density（g/cm3） | 0.15~0.35 |
| 耐折性(常温）(4万次裂口长度，mm)Folding endurance (room temperature)(40,000 gap length mm) | ＜8 |
●配合比率是以最佳配比值为基础，此配比值会随添加的颜料助剂种类和添加量不同而变化。
Matching ratio is based on the optimal matching value which will vary with the category and additive amount of paint additives added.
●自由泡沫密度会依季节（温度，湿度）的不同而变化。
Free foam density will vary with the seasons (temperature, humidity).
●脱模时间会随成型品厚度的增加而延长。
Stripping time will be extended with the increase of the thickness of moldings.
●耐折条件：屈挠角度为 90度，频率为80次/min*4万次。
Folding endurance conditions: bending angle is 90 degrees and the frequency is 80 times / min * 40 thousand times
● 以上数据仅作参考，具体数据以实际操作为准。如需其他物性指标，请与我公司联系。
Data listed above is just for reference. The specific data is subjected to the practical operation. If other physical properties are required, please contact us.